MICROSTRUCTURE OF THE GAS TRANSMISSION PIPE SEGMENT BASE METAL AFTER THE CONTINIOUS SERVICE

Research output: Contribution to journalArticleResearchpeer-review

Abstract

The microstructure of the transmission gas pipeline part was studied. The part was discarded under the results of the magnetic inspection and visual control. Areas located near the outer surface of the tube on the transverse microsections were under consideration. The origin of the surface defects was defined. They were formed during the hot rolling of the sheet, which was used for the pipe manufacturing, they were not developed during the service time. A quantitative description of the main structural components, i. e. ferrite and pearlite, was conducted. The chemical composition of the prevailing non-metallic inclusions was determined and their morphology was described. Despite the presence of the large irregular shape particles, any secondary cracks formed during pipeline service were not detected in the part under consideration. Thus, the presence of the inner and surface defects did not cause any collapse of the transmission gas pipeline, possibly due to their morphological characteristics
Translated title of the contributionMICROSTRUCTURE OF THE GAS TRANSMISSION PIPE SEGMENT BASE METAL AFTER THE CONTINIOUS SERVICE
Original languageRussian
Pages (from-to)48
Number of pages1
JournalСовременные проблемы науки и образования
Issue number1-1
Publication statusPublished - 2015

Fingerprint

Surface defects
Gas pipelines
Pipe
Microstructure
Pearlite
Hot rolling
Metals
Gases
Ferrite
Pipelines
Inspection
Cracks
Chemical analysis

GRNTI

  • 52.13.00

Level of Research Output

  • VAK List

Cite this

@article{d6649ea046de407bb04645b8c53eb681,
title = "МИКРОСТРУКТУРА ОСНОВНОГО МЕТАЛЛА ФРАГМЕНТА МАГИСТРАЛЬНОГО ГАЗОПРОВОДА ПОСЛЕ ДЛИТЕЛЬНОЙ ЭКСПЛУАТАЦИИ",
abstract = "В работе изучена микроструктура фрагмента трубы магистрального газопровода, отбракованного по результатам инспекции, осуществленной после проведения внутритрубной дефектоскопии. На поперечных шлифах исследованы участки, расположенные вблизи внешней поверхности трубы, определена причина появления дефектов, наблюдаемых на поверхности. Дефекты сформировались при горячей прокатке листа, из которого была изготовлена труба, и не получили дальнейшего развития при эксплуатации. Также проведена количественная оценка основных структурных составляющих – феррита и перлита, определен химический состав преобладающих неметаллических включений и описана их морфология. Несмотря на присутствие в структуре вблизи внутренней поверхности трубы крупных включений неправильной формы, в их окрестностях вторичных трещин не обнаружено. Таким образом, наличие внутренних и поверхностных дефектов не сказалось на успешной эксплуатации газопровода в течение 20 лет, что, скорее всего, связано с морфологическими особенностями зарегистрированных дефектов.",
author = "Рыжков, {Максим Александрович} and Сукнева, {А. А.} and Юровских, {Артем Сергеевич} and Буров, {Сергей Владимирович} and Майсурадзе, {Михаил Васильевич}",
year = "2015",
language = "Русский",
pages = "48",
journal = "Современные проблемы науки и образования",
issn = "2070-7428",
publisher = "Общество с ограниченной ответственностью {"}Издательский Дом {"}Академия Естествознания{"}",
number = "1-1",

}

TY - JOUR

T1 - МИКРОСТРУКТУРА ОСНОВНОГО МЕТАЛЛА ФРАГМЕНТА МАГИСТРАЛЬНОГО ГАЗОПРОВОДА ПОСЛЕ ДЛИТЕЛЬНОЙ ЭКСПЛУАТАЦИИ

AU - Рыжков, Максим Александрович

AU - Сукнева, А. А.

AU - Юровских, Артем Сергеевич

AU - Буров, Сергей Владимирович

AU - Майсурадзе, Михаил Васильевич

PY - 2015

Y1 - 2015

N2 - В работе изучена микроструктура фрагмента трубы магистрального газопровода, отбракованного по результатам инспекции, осуществленной после проведения внутритрубной дефектоскопии. На поперечных шлифах исследованы участки, расположенные вблизи внешней поверхности трубы, определена причина появления дефектов, наблюдаемых на поверхности. Дефекты сформировались при горячей прокатке листа, из которого была изготовлена труба, и не получили дальнейшего развития при эксплуатации. Также проведена количественная оценка основных структурных составляющих – феррита и перлита, определен химический состав преобладающих неметаллических включений и описана их морфология. Несмотря на присутствие в структуре вблизи внутренней поверхности трубы крупных включений неправильной формы, в их окрестностях вторичных трещин не обнаружено. Таким образом, наличие внутренних и поверхностных дефектов не сказалось на успешной эксплуатации газопровода в течение 20 лет, что, скорее всего, связано с морфологическими особенностями зарегистрированных дефектов.

AB - В работе изучена микроструктура фрагмента трубы магистрального газопровода, отбракованного по результатам инспекции, осуществленной после проведения внутритрубной дефектоскопии. На поперечных шлифах исследованы участки, расположенные вблизи внешней поверхности трубы, определена причина появления дефектов, наблюдаемых на поверхности. Дефекты сформировались при горячей прокатке листа, из которого была изготовлена труба, и не получили дальнейшего развития при эксплуатации. Также проведена количественная оценка основных структурных составляющих – феррита и перлита, определен химический состав преобладающих неметаллических включений и описана их морфология. Несмотря на присутствие в структуре вблизи внутренней поверхности трубы крупных включений неправильной формы, в их окрестностях вторичных трещин не обнаружено. Таким образом, наличие внутренних и поверхностных дефектов не сказалось на успешной эксплуатации газопровода в течение 20 лет, что, скорее всего, связано с морфологическими особенностями зарегистрированных дефектов.

UR - https://elibrary.ru/item.asp?id=25323070

M3 - Статья

SP - 48

JO - Современные проблемы науки и образования

JF - Современные проблемы науки и образования

SN - 2070-7428

IS - 1-1

ER -