Brusnitsyn S., Mysik R., Sulitsin A., Ozhgikhin I. Influence of continuous cast bar quality on cracks formation in the copper rod. In this paper the effect of the main sources of gas saturation of the copper melt at Contirod technological method for copper rod manufacturing on probability of continuous cast bar gas defects formation was studied. Metallographic analysis of continuous cast bar samples was carried out. Set the average pore size of the gas volume fraction and porosity. The average gas pores size and gas porosity volume fraction were determined. Updating of technological regimes of continuous casting will reduce the chance of copper rod cracking during the standard torsion testing.
Título traducido de la contribuciónInfluence of continuous cast bar quality on cracks formation in the copper rod
Idioma originalRussian
Páginas (desde-hasta)27-31
Número de páginas5
PublicaciónЛитейщик России
N.º10
EstadoPublished - 2014

GRNTI

  • 55.15.00

Level of Research Output

  • VAK List

Huella Profundice en los temas de investigación de 'ВЛИЯНИЕ КАЧЕСТВА НЕПРЕРЫВНОЛИТОЙ ЗАГОТОВКИ НА ОБРАЗОВАНИЕ ТРЕЩИН В МЕДНОЙ КАТАНКЕ'. En conjunto forman una huella única.

Citar esto