ГИДРОХИМИЧЕСКИЙ СИНТЕЗ ПЛЕНОК ХАЛЬКОГЕНИДОВ МЕТАЛЛОВ. ЧАСТЬ 22. ТЕРМИЧЕСКАЯ СТАБИЛЬНОСТЬ ПЛЕНОК ГИДРОХИМИЧЕСКИ ОСАЖДЕННЫХ ПЕРЕСЫЩЕННЫХ ТВЕРДЫХ РАСТВОРОВ CDXPB1-ХS

Resultado de la investigación: Articlerevisión exhaustiva

Resumen

It was found that the upper temperature limit of stability of hydrochemical deposited supersaturated solid solutions СdxPb1-xS (0 < x ≤ 0.18) is 405-410 K. At higher temperatures, heating decomposes these compounds in two phases: a solid solution with the equilibrium at a given temperature sulfide content cadmium and X-ray amorphous CdS. The greatest changes in the photovoltaic properties of the films of supersaturated solid solutions CdxPb1-xS during the first two years of storage at room conditions were observed in the first 2-3 months. Dark resistance varied by 20-40% during this period, the maximum change in voltage sensitivity was 20-25% of the original value.
Título traducido de la contribuciónHydrochemical synthesis of metal chalcogenide films. Part 22. Thermal stability of hydrochemically deposited CdxPb1-xS supersaturated solid solutions
Idioma originalRussian
Páginas (desde-hasta)92-97
Número de páginas6
PublicaciónБутлеровские сообщения
Volumen39
N.º9
EstadoPublished - 2014

GRNTI

  • 29.00.00 PHYSICS

Level of Research Output

  • VAK List

Huella

Profundice en los temas de investigación de 'ГИДРОХИМИЧЕСКИЙ СИНТЕЗ ПЛЕНОК ХАЛЬКОГЕНИДОВ МЕТАЛЛОВ. ЧАСТЬ 22. ТЕРМИЧЕСКАЯ СТАБИЛЬНОСТЬ ПЛЕНОК ГИДРОХИМИЧЕСКИ ОСАЖДЕННЫХ ПЕРЕСЫЩЕННЫХ ТВЕРДЫХ РАСТВОРОВ CDXPB1-ХS'. En conjunto forman una huella única.

Citar esto