МИКРОСТРУКТУРА И МЕХАНИЧЕСКИЕ СВОЙСТВА ВЫСОКОПРОЧНОЙ МАШИНОСТРОИТЕЛЬНОЙ СТАЛИ МАРТЕНСИТНОГО КЛАССА

Resultado de la investigación: Article

Resumen

A promising martensitic steel with high hardenability was studied. In the range of cooling rates 0.1…30 °C/s the only one transformation was registered by the dilatometer starting at a temperature of M s = 355 ± 10 °C. The microstructure and mechanical properties of the studied steel were analyzed after various heat treatment modes: cooling from austenitizing temperature with various rates (from 0.02 to 20 °C/s), austempering at a temperature 280…380 °C, oil quenching and tempering at a temperature 200…600 °C. It is shown that a 1000-fold change in the cooling rate weakly affects the strength of the studied steel. The bainitic transformation in the steel under consideration occurred in the temperature range of the martensitic transformation, which led to a decrease in impact toughness compared to the fully martensitic microstructure both after slow cooling and austempering.
Título traducido de la contribuciónMICROSTRUCTURE AND MECHANICAL PROPERTIES OF MARTENSITIC HIGH-STRENGTH ENGINEERING STEEL
Idioma originalRussian
Páginas (desde-hasta)41-49
Número de páginas9
PublicaciónМеталлург
N.º7
EstadoPublished - 2020

GRNTI

  • 53.00.00 METALLURGY

Level of Research Output

  • VAK List

Huella Profundice en los temas de investigación de 'МИКРОСТРУКТУРА И МЕХАНИЧЕСКИЕ СВОЙСТВА ВЫСОКОПРОЧНОЙ МАШИНОСТРОИТЕЛЬНОЙ СТАЛИ МАРТЕНСИТНОГО КЛАССА'. En conjunto forman una huella única.

Citar esto