ФОРМИРОВАНИЕ ДИССИПАТИВНОЙ СТРУКТУРЫ МЕТАСТАБИЛЬНОГО АУСТЕНИТА ДЛЯ ПОВЫШЕНИЯ АБРАЗИВНОЙ ИЗНОСОСТОЙКОСТИ СТАЛЕЙ ПЕРЛИТНОГО И ЛЕДЕБУРИТНОГО КЛАССОВ

Resultado de la investigación: Articlerevisión exhaustiva

Resumen

The structure of retained austenite in wear-resistant steels 150KhNML and Kh12MFL of pearlitic and ledeburitic classes is studied under the conditions of abrasive wear after different variants of heat treatment. The working surfaces of the steels are subjected to electron microscope transmission analysis. It is shown that the retained austenite formed as a result of high-temperature quenching (1100 - 1170°C) is metastable and transforms into fine- and nanocrystalline strain martensite with regular periodic arrangement of crystals in the wear process in addition to slip and twinning. This provides a high capacity of the working surface for friction hardening. The optimum mode of heat treatment for formation of a dissipative structure with high abrasive wear resistance is chosen.
Título traducido de la contribuciónFormation of dissipative structure of metastable austenite for raising the abrasive wear resistance of steels of pearlitic and ledeburitic classes
Idioma originalRussian
Páginas (desde-hasta)30-39
Número de páginas10
PublicaciónМеталловедение и термическая обработка металлов
N.º3 (777)
EstadoPublished - 2020

GRNTI

  • 53.00.00 METALLURGY

Level of Research Output

  • VAK List

Huella

Profundice en los temas de investigación de 'ФОРМИРОВАНИЕ ДИССИПАТИВНОЙ СТРУКТУРЫ МЕТАСТАБИЛЬНОГО АУСТЕНИТА ДЛЯ ПОВЫШЕНИЯ АБРАЗИВНОЙ ИЗНОСОСТОЙКОСТИ СТАЛЕЙ ПЕРЛИТНОГО И ЛЕДЕБУРИТНОГО КЛАССОВ'. En conjunto forman una huella única.

Citar esto