ВЛИЯНИЕ ОТЖИГА В ФЕРРОМАГНИТНОМ СОСТОЯНИИ НА СТРУКТУРУ СПЛАВА ЖЕЛЕЗА С 18 AT.% ГАЛЛИЯ

Ю. П. Черненков, Н. В. Ершов, Вера Анатольевна Лукшина

Resultado de pesquisa: Article

Resumo

The atomic structure of the iron–gallium alloy containing 18 at % Ga has been studied by X-ray diffraction. The samples were annealed in the paramagnetic ( T > T _C) and ferromagnetic ( T < T _C) state. In the first case, the structural state was fixed by quenching from the annealing temperature into water; in the second case, the structural state was obtained by slow cooling. The structural studies of the single-crystal samples were conducted on a four-circle X-ray diffractometer at room temperature. From the X-ray diffraction data, it follows that the alloy, independently on the heat treatment, contains B 2 clusters, i.e., locally ordered regions with the CsCl-type structure observed in alloys of iron with silicon (to 10 at % Si) and aluminum (7 at % Al) before. In addition to the B 2‑clusters, regions with the D 0_3 short-range order are observed in the quenched sample; the sizes of these regions significantly increases after annealing in the ferromagnetic state, i.e., a long-range order forms. The relation of the fine structural changes in the alloy due to various heat treatments with its magnetoelastic and magnetostriction properties is discussed.
Título traduzido da contribuiçãoEffect of Annealing in a Ferromagnetic State on the Structure of an Fe–18 at % Ga Alloy
Idioma originalRussian
Páginas (de-até)12-21
RevistaФизика твердого тела
Volume61
Número de emissão1
DOIs
Estado da publicaçãoPublished - 2019

GRNTI

  • 29.00.00 PHYSICS

Level of Research Output

  • VAK List

Impressão digital Mergulhe nos tópicos de investigação de “ВЛИЯНИЕ ОТЖИГА В ФЕРРОМАГНИТНОМ СОСТОЯНИИ НА СТРУКТУРУ СПЛАВА ЖЕЛЕЗА С 18 AT.% ГАЛЛИЯ“. Em conjunto formam uma impressão digital única.

Citar isto