摘要

Polycrystalline films of CdxPb1-x S (0.021 ≤ x ≤ 0.090) supersaturated substitutional solid solutions with a cubic structure B1 (Fm3¯m space group) have been obtained with varying cadmium acetate salt Cd(CH3COO)2 in the reaction mixture within 0.01-0.1 mol/l on the sitall substrates. Their thickness changed from ~ 0.4 to ~ 1.0 microns. A correlation has been established between the structural-morphological and functional properties of CdxPb1-x S thin-film layers. The extreme character of the voltage sensitivity dependence on the cadmium salt concentration in the reaction bath is associated with the nonmonotonic introduction of cadmium into the PbS crystal lattice. It is shown that the maximum photocurrent is possessed by CdxPb1-x S thin-film layers formed from crystallites with pronounced faceting. We have found the surface sensitivity of the CdxPb1-xS films to the presence of ~ 0.02 mg/m3 NO2 in the air, which is significantly lower than the maximum allowable concentration.
投稿的翻译标题STRUCTURE AND MORPHOLOGY EFFECTS ON SENSING PROPERTIES CDXPB1-XS FILMS
源语言Russian
页(从-至)1186-1194
页数9
期刊Физика и техника полупроводников
55
12
DOI
Published - 2021

GRNTI

  • 31.00.00 CHEMISTRY

Level of Research Output

  • VAK List

指纹

探究 'ВЛИЯНИЕ СТРУКТУРНО-МОРФОЛОГИЧЕСКИХ ХАРАКТЕРИСТИК НА СЕНСОРНЫЕ СВОЙСТВА ПЛЕНОК CD<sub>X</sub>PB<sub>1-X</sub>S' 的科研主题。它们共同构成独一无二的指纹。

引用此