ИССЛЕДОВАНИЕ ПОКРЫТИЙ TiAlSiN ПОЛУЧЕННЫХ МЕТОДОМ РЕАКТИВНОГО МАГНЕТРОННОГО РАСПЫЛЕНИЯ В УСЛОВИЯХ СИЛЬНОТОЧНОГО ИОННОГО АССИСТИРОВАНИЯ

科研成果: Article

摘要

Nanocomposite TiAlSiN coatings were deposited by reactive magnetron sputtering with changing of the ratio of the ion current density j) and the flux of condensing atoms jn in a wide range 5-25. To generate plasma in a working chamber, a broad (80 cm2) beam of low-energy (100 eV) electrons was used. The beam current varied from 5 to 30 A and provided changing ofj in a range of 1.8-9 mA/cm2. The effect of j/j changing on properties of coating was investigated. The increasing of j/j, was shown to be accompanied by non-monotonous variation of hardness and texture of coatings as a result of changing of residual stresses. The value j/j, corresponded to maximum hardness (43 GPa) of coatings was defined. The excess of this value was shown to lead to residual stress relaxation and decreasing of the hardness up to 36 GPa.
投稿的翻译标题Investigation of TiAlSiN Coatings Deposited by Reactive Magnetron Sputtering under High-Current Ion Assistance
源语言Russian
页(从-至)106-112
页数7
期刊Поверхность. Рентгеновские, синхротронные и нейтронные исследования
6
DOI
Published - 2017

GRNTI

  • 29.00.00 PHYSICS

Level of Research Output

  • VAK List

指纹 探究 'ИССЛЕДОВАНИЕ ПОКРЫТИЙ TiAlSiN ПОЛУЧЕННЫХ МЕТОДОМ РЕАКТИВНОГО МАГНЕТРОННОГО РАСПЫЛЕНИЯ В УСЛОВИЯХ СИЛЬНОТОЧНОГО ИОННОГО АССИСТИРОВАНИЯ' 的科研主题。它们共同构成独一无二的指纹。

引用此