ПОЛУЧЕНИЕ И ЭЛЕКТРОХИМИЧЕСКИЕ СВОЙСТВА ДВОЙНЫХ ЛИТИЙ-ЗАМЕЩЕННЫХ НАТРИЙ-ВАНАДИЕВЫХ БРОНЗ

科研成果: Article同行评审

摘要

Lithium-substituted sodium-vanadium bronzes of the Na2 –хLiхV12O30 (OVB) (0.6 ≤ x ≤ ≤ 1.4) were obtained from sodium and lithium formates and vanadyl formate VO(HCOO)2·H2O using soft chemistry methods. Electrochemical cycling of cells with a cathode and an anode from them, as well as with a molten lithium anode and an electrolyte based on lithium hexa-oxo zirconate was performed. It is shown, that lithium cations reversibly intercalate into bronzes of the Na2– хLiхV12O30 composition at high temperatures of 460–560°C. Using scanning electron spectroscopy (SEM) it was shown that Na2 – хLiхV12O30 OVB crystals decompose into thin plate aggregates after cycling. According to the results of energy-dispersive X-ray analysis (EDRA) it was found that there is an uneven distribution of sodium in the crystallites of the OVB phase after cycling, while maintaining the phase composition. The use of double lithium-sodium vanadium bronzes Na2 ‒ хLiхV12O30 together with lithium-conducting solid electrolytes is promising and requires further research.
投稿的翻译标题SYNTHESIS AND ELECTROCHEMICAL PROPERTIES OF DOUBLE LITHIUM-SUBSTITUTED SODIUM-VANADIUM BRONZES
源语言Russian
页(从-至)406-415
页数10
期刊Расплавы
4
DOI
Published - 2021

GRNTI

  • 31.00.00 CHEMISTRY

Level of Research Output

  • VAK List

指纹

探究 'ПОЛУЧЕНИЕ И ЭЛЕКТРОХИМИЧЕСКИЕ СВОЙСТВА ДВОЙНЫХ ЛИТИЙ-ЗАМЕЩЕННЫХ НАТРИЙ-ВАНАДИЕВЫХ БРОНЗ' 的科研主题。它们共同构成独一无二的指纹。

引用此